Effect of fiber surface treatment on mechanical, interfacial, and moisture absorption properties of cattail fiber-reinforced composites

AUTHORS

Md Shadhin, Raghavan Jayaraman, Mashiur Rahman, Danny Mann

ABSTRACT

Surface treatment of cattail, a lignocellulosic renewable fiber, was investigated to determine the conditions that would reduce moisture absorption while maximizing the properties of cattail fiber-reinforced unsaturated polyester composites. Surface modification of cattail fiber was studied by treating them with 2.5, 5, and 10% of 1,6-diisocyanatohexane (DIH) and 2-hydroxyethyl acrylate (HEA) for three different immersion times (10, 20, and 30 min). DIH-HEA treated fibers were preformed into a non-woven mat and impregnated with unsaturated polyester resin to manufacture composite. The existence of covalent bonds on the treated fibers via NH and CN groups was confirmed by FTIR spectroscopy. The 10% DIH-HEA resulted in the best results; while the mean diameter of the treated fiber decreased by ~37%, the modulus and the strength of it increased by ~267 and ~151%, respectively. Equilibrium moisture regain of the treated fibers and their composites decreased by ~43% and ~40%, respectively. The tensile modulus of the composites increased by ~171%. Enhancement in tensile strength is observed but could not be quantified due to the difference in Vf and scatter in the data. SEM examination confirmed the enhancement in fiber–matrix bonding due to surface treatment.

Probabilistic model for cattail and canola fibers: effect of environmental conditions, structural parameters, fiber length, and estimators

AUTHORS

Md Shadhin, Danny Mann, Mashiur Rahman

ABSTRACT

Biomass fibers are being widely investigated for industrial applications as an alternative to synthetic fibers using a standard humidity condition. In this study, the mechanical properties of two waste biomass fibers – canola and cattail – have been investigated when subjected to different environmental conditions, fiber length, and type of estimators used during analysis. The effect of different environmental conditions and structural variations were investigated by measuring the tensile properties after exposing them to eight different relative humidity conditions using a fixed fiber length of 25 mm. Further investigation was conducted using fiber lengths of 25, 35 and 45 mm using the most conservative relative humidity condition. The data were analyzed by a Weibull distribution model using four different estimators. The results revealed that Weibull strength (σavg) and modulus (Eavg) closely followed experimental values for cattail and canola fibers. The different relative humidity conditions and fiber lengths resulted in different Weibull parameters with 11% relative humidity and the mean rank estimator predicted the most conservative tensile strength for both waste biomass fibers. The experimental and characteristic Weibull strength decreased when fiber gauge length increased from 25 to 45 mm. The tensile strength and modulus of both waste biomass fibers at 50% reliability lie within the range of average experimental values. However, these values are reduced to 155 MPa (strength) and 20 GPa (modulus) for cattail fiber at 90% reliability. The survival probability of the tensile strength and modulus were found to be the highest at 75% and 100% relative humidity for cattail and canola fibers, respectively.